鋼種
|
化學成份 (%)
|
最高工作溫度
|
特性
|
|||||
C
|
Si
|
Mn
|
Ni
|
Cr
|
Mo
|
|||
1cr13
|
≤ 0.15
|
≤ 0.6
|
≤ 0.6
|
-
|
12-14
|
-
|
650 °
|
普通網帶
|
1cr17
|
≤ 0.15
|
≤ 0.6
|
≤ 0.6
|
-
|
12-18
|
-
|
650 °
|
普通網帶
|
304M
|
≤ 0.06
|
≤ 1.0
|
≤ 2.0
|
8.9-10.0
|
18-20
|
-
|
920 °
|
普通網帶
|
304L
|
≤ 0.03
|
≤ 1.0
|
≤ 2.0
|
9-13
|
18-20
|
-
|
-
|
耐晶界腐蝕
|
316
|
≤ 0.08
|
≤ 1.0
|
≤ 2.0
|
10-14
|
16-18
|
2-3
|
-
|
耐腐蝕
|
316L
|
≤ 0.03
|
≤ 1.0
|
≤ 2.0
|
12-15
|
16-18
|
2-3
|
-
|
耐晶界腐蝕
|
309S
|
≤ 0.08
|
≤ 1.0
|
≤ 2.0
|
12-15
|
22-24
|
-
|
1000 °
|
耐長時間高溫
|
310S
|
≤ 0.08
|
≤ 1.5
|
≤ 2.0
|
19-22
|
24-26
|
-
|
1100 °
|
耐高溫及高溫沖擊、抗高溫循環
|
314
|
≤ 0.25
|
≤ 1.5-3.0
|
≤ 2.0
|
19-22
|
23-26
|
-
|
1200 °
|
在 310 基礎上提高抗氧性
|
CI20NI80
|
≤ 0.15
|
≤ 0.4-1.3
|
≤ 0.7
|
75-78
|
20-23
|
-
|
1200 °
|
耐高溫、抗氧化
|